The ASTM B specification covers the requirements for a coating of zinc mechanically deposited on iron and steel basis metals. The coating. governing specifications for hot-dip galvanizing; ASTM. A, A, and A as .. requirements specified in ASTM B range from. to mils (5 to ASTM B Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel.

Author: JoJozshura Vudogal
Country: Liberia
Language: English (Spanish)
Genre: Photos
Published (Last): 28 May 2007
Pages: 285
PDF File Size: 6.88 Mb
ePub File Size: 5.67 Mb
ISBN: 273-3-33591-126-1
Downloads: 7567
Price: Free* [*Free Regsitration Required]
Uploader: Zushura

Mechanical Galvanizing does not fill valleys of threaded fasteners and their parts mate quickly and easily. If an application requires torqueing, exposure to astk or any handling that could rupture a finish, mechanical plating provides durable metal coating with excellent adhesion. Once the plating reaches the desired g695 the parts are then dried and post-plating finishes are applied if required.

Apparently, this ASTM standard uses a mechanical means to place zinc onto the metal surface and this approach is reported to be better then the hot dip method which can have the zinc flake off.

Parts breakages because of hydrogen embrittlement need not be a problem of parts are plated mechanically and are not used for a minimum of 48 hours after plating.

Defense manufacturing is all about project manufacturing and project accounting.

ASTM B695-04

Uniformity of thickness depends on part size and shape with typically thinner deposits on edges and thicker deposits in recesses.

Also – My application are exposed structural steel members that are placed in GUAM heavy salt marine environmentwhich method would you use for corrosion protection OR if you know of a better way for corrosion protection, please share it.

  LINGUAGEM ASSEMBLY 8086 PDF

b6995

Click Here to join Eng-Tips and talk with other members! The Eng-Tips staff will check this out and take appropriate action.

The Ability to plate parts, which tangle the glass impact media used in the process, tends to prevent parts from tangling. We, as qualified professionals, can plate low carbon steel, cold rolled steel, high carbon heat-treated steel, various tool steels, high strength alloys, free-mechanical steels including leaded steels.

Electroplating The main advantage of mechanical plating over electroplating is the elimination of hydrogen embrittlement. Appearance is uniform comparatively smooth with a satiny texture and has none of the discolored and mottled effect o hot-dip galvanizing. Is there an ASTM that provides a standard for the high-build organic coating? This mechanical plating process characteristically makes this technology an ideal choice for plating hardened steel springs.

Mechanical Galvanizing is a room temperature process that does not detemper heat-treated parts. Because Mechanical Galvanizing is an extension of mechanical plating technology; it does not produce hydrogen embrittlement and does not require lengthy non-reliable post-plate baking cycles.

ASTM B – Haydon BoltsHaydon Bolts

It’s easy to join and it’s free. Thickness depends only on the amount of zinc powder. Mechanical Galvanizing produces parts that are ready to use without any further processing steps.

This makes mechanical plating an ideal process for plating flat stampings and washers. Because of the composite nature of mechanical coating, this naturally lubricated coating will not gall, producing more accurate torque-tension relationship.

ASTM B for coating of Zinc mechanically onto IRON/STEEL. – Corrosion engineering – Eng-Tips

Click here for a quote or call us at Any metal that can be made into a fine powder can be mechanically plated, however CIP specializes in zinc, tin, and aluminum. CIP is certified asrm work with coating for zinc deposited mechanically onto iron and steel b6995 metals. Work Item s – proposed revisions of this standard. The thickest coating classes are usually referred to as “mechanically galvanized”. What is Hydrogen Embrittlement Hydrogen embrittlement is a phenomenon which causes materials to lose their strength and become brittle.

  LOS CAUTIVERIOS DE LAS MUJERES MARCELA LAGARDE PDF

The base metal is less chemically active s o that the coating corrodes first. The zinc coatings are classified according to thickness and identified into two types; as coated without supplementary treatments or with colored chromate conversion treatment.

Batch to batch conformity: CIP offers two post-plating services: Mechanical plating is he method preferred by many engineers for hardened fasteners and stressed components.

Custom Industrial Processing, Inc. This abstract is a brief summary of the referenced standard. You get the benefit of metallurgical bond and the iron-zinc intermetallics formed by dipping into molten zinc at high temperature. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application.